%7B%22isLastPage%22%3Atrue%2C%22notes%22%3A%5B%7B%22type%22%3A%22post%22%2C%22targetId%22%3A%22845904%22%2C%22notes%22%3A%5B%5D%7D%2C%7B%22type%22%3A%22post%22%2C%22targetId%22%3A%22845933%22%2C%22notes%22%3A%5B%5D%7D%2C%7B%22type%22%3A%22post%22%2C%22targetId%22%3A%22846113%22%2C%22notes%22%3A%5B%5D%7D%2C%7B%22type%22%3A%22post%22%2C%22targetId%22%3A%22846114%22%2C%22notes%22%3A%5B%5D%7D%2C%7B%22type%22%3A%22post%22%2C%22targetId%22%3A%22846115%22%2C%22notes%22%3A%5B%5D%7D%2C%7B%22type%22%3A%22post%22%2C%22targetId%22%3A%22846674%22%2C%22notes%22%3A%5B%5D%7D%5D%2C%22pid%22%3A%22845904%22%2C%22tid%22%3A%2282826%22%2C%22mainForumsId%22%3A%5B%2283%22%5D%2C%22categoriesId%22%3A%5B%22%22%5D%2C%22tcId%22%3A%5B%5D%7D
%7B%22isEditMode%22%3Afalse%7D
中学生在中科院搞事情之——锂硫电池相关实验
在 https://www.kechuang.org/t/82712 帖子中，我介绍了我制备载硫石墨烯的实验(严格的讲，应该叫“载硫还原氧化石墨烯”，性能与载硫石墨烯有区别，但是满足实验要求)。接下来我将用制得的载硫石墨烯作为正极材料，组装并测试锂硫电池。【长期工程】
今天的任务是配制正极浆料，并进行涂片。大部分操作由我完成，图比较少。
1.取一部分载硫石墨烯，称量得其质量为0.0302g。按照8:1:1的比例计算得到，导电炭黑和PVDF的质量均为0.003775g，考虑到称量精度问题，称量0.0038g(但其实最后一位精确度不高，试剂质量可能有较大差异，下次可以通过增大载硫石墨烯的质量减小误差)。
2.将称出的三种物质混合，加入适量1-甲基-2-吡咯烷酮(这个量没有一定之规，0.5ml左右即可)，磁力搅拌约1h。![IMG_20180506_100248_1.jpg]()
今天的任务是配制正极浆料，并进行涂片。大部分操作由我完成，图比较少。
1.取一部分载硫石墨烯，称量得其质量为0.0302g。按照8:1:1的比例计算得到，导电炭黑和PVDF的质量均为0.003775g，考虑到称量精度问题，称量0.0038g(但其实最后一位精确度不高，试剂质量可能有较大差异，下次可以通过增大载硫石墨烯的质量减小误差)。
2.将称出的三种物质混合，加入适量1-甲基-2-吡咯烷酮(这个量没有一定之规，0.5ml左右即可)，磁力搅拌约1h。
[修改于 6年11个月前 - 2018/05/14 15:56:07]
引用
加载评论中，请稍候...
200字以内，仅用于支线交流，主线讨论请采用回复功能。
p.s.:与导师交流关于rGO(还原氧化石墨烯)上的缺陷得知:rGO上的缺陷对锂硫电池的部分性能(如载硫稳定性、飞梭效应的降低)有帮助，对导电性能则有不利影响，需要找到一个平衡。一般方法制得的rGO缺陷数量接近合适的值。